S165M

We could produce AISI S165M,SS 2387 Forged forging stainless Steel Round Bars Rods Square rectangular rectangle Flat Hex Bars,AISI S165M,SS 2387 Forged Forging Steel Hollow Bars Forged Forging Sleeves Bushes Bushing Pipes Piping tube tubings barrels Casing Cases Shells cylinders hubs housings,AISI S165M,SS 2387 Seamless Rolled Steel Rings AISI S165M,SS 2387 Forged Forging Steel rings,AISI S165M,SS 2387 Forged Forging Steel Blocks Discs Disks Plates ,AISI S165M,SS 2387 Forged Forging Steel hydroelectric Hydraulic Kaplan Hydro Power Water turbine blades,AISI S165M,SS 2387 forged forging steel pump shafts spindles,injector bodies.AISI S165M,SS 2387 forged forging Centrifugal Machines Disc Stack Decanter Centrifuge Bowl Body Bodies Hood Covers,and other AISI S165M,SS 2387 forged forging parts forged forging pieces forged forging steel components materials as per the requirement of the clients

Type Analysis

Single figures are nominal except where noted.

Carbon (Maximum) 0.06 % Manganese (Maximum) 1.50 % Phosphorus (Maximum) 0.040 % Sulfur (Maximum) 0.030 % Silicon (Maximum) 0.70 % Chromium 16.00 % Nickel 5.00 % Molybdenum 1.20 % Nitrogen (Minimum) 0.02 % Iron Balance

S165M Stainless is a martensitic stainless steel specially designed for those applications requiring high mechanical properties combined with improved corrosion resistance relative to traditional martensitic steels.

S165M Stainless is also offered as an enhanced machining variant, S165M  stainless, which obtains an enhanced machinability characteristic through controlled addition of sulfur without degrading strength or corrosion resistance. S165M EM Stainless contains differentiated micro constituents for easier machining production.

Corrosion Resistance

This alloy shows good corrosion resistance to mild atmospheres, both in annealed and heat-treated conditions. It resists corrosion in many industrial and domestic environments as well as potable and mine waters.

For optimum corrosion resistance, surfaces must be free of scale, lubricants, foreign particles, and coatings applied for drawing and heading. After fabrication of parts, cleaning and/or passivation should be considered.

Annealing

This alloy is typically annealed at 1112°F - 1200°F (600°C - 650°C), followed by slow cooling in air. Heat uniformly to the selected temperature.

Hardening

Heat to 1740°F - 1920°F (950°C - 1050°C), followed by oil quench. Small sections can be hardening by air cool.

Tempering

QT900 properties are achieved by tempering at 1025°F - 1145°F (550°C - 620°C) for 8 hours followed by oil or air cool. Alternately, material may be treated using two cycles, 4 hours each followed by oil or air cool. This alloy may suffer temper embrittlement if tempered at 785°F - 1022°F (450°C - 550°C), or slow cool at this temperature range.

Our S165M forging rings will be Ultrasonic testing as per standard, EN10228-3,Sep1921,ASTM A388 and so on

We could supply S165M stainless steel forging parts certificate as per the standard of EN10204-3.1 or EN10204-3.2 of third party

Please send us the size or drawing of S165M forged material that you need, we are glad to quote the best price for your side